3M Scotch-Weld DP100 Plus Clear - 4 Minute Flexible Fast Set Epoxy

In stock
SKU: 3M_DP100PCL_050ML
Which Kit do you Need?
Regular price $ 47.42 USD
20 units are available

Product details

  • Type Epoxy
  • Vendor 3M Scotch-Weld
  • SKU 3M_DP100PCL_050ML
  • Barcode 751354334517

3M™ Scotch-Weld™ Epoxy Adhesive DP100 Plus Clear is a fast setting, two-part, 1:1 mix ratio mercaptan-cured epoxy adhesive. It is unique among fast setting mercaptan cure epoxies in that it combines high shear strength with good peel performance properties. Scotch-Weld epoxy adhesive DP100 Plus Clear is transparent and slightly flexible when cured.

Features:

  • 4 Minute Work Life
  • High Shear & Peel Strength
  • Slightly Flexible When Cured

Overlap Shear Strength (OLS) vs. Temperature:

(Bonds cured 24 hours @ room temperature (RT) + 2 hrs @ 160°F [71°C])

Etched Aluminum

3500 psi

Sanded Aluminum (60 grit)

1800 psi

Cold Rolled Steel

1700 psi

Wood,Fir

700 psi

Glass, Borosilicate

250 psi

Glass, +3M™ Scotch-Weld™ Primer EC3901

300 psi

Polycarbonate

600 psi

Acrylic

300 psi

Fiberglass

1500 psi

ABS

280 psi

PVC

450 psi

Polypropylene

80 psi

Rate of Strength Build-Up (OLS on Etched Aluminum) Bonds tested after:

1 hr @ RT

600 psi

6 hrs @ RT

900 psi

24 hrs @ RT

1100 psi

7 days @ RT

2800 psi

1 mo @ RT

3400 psi

Environmental Aging: (OLS on Etched Aluminum)Bonds tested after:

24hrsRT+ 2 hrs @ 160°F (71°C)

3500psi

24hrsRT+ 2 hrs @ 240°F (116°C)

4500psi

1 wk RT + 1 wk @ 90°F (32°C)/90% RH

3900psi

1 wk RT + 1 wk 248°F (120°C)

4500psi

1 wk RT + 1 wk H2O immersion

3500psi

Overlap shear (OLS) strengths were measured on1 in. wide 1/2 in. overlap specimens. These bonds were made individually using 1 in. x 4 in. pieces of substrate. The thickness of the bond line was 0.005-0.008 in. All strengths were measured at 70°F (21°C) except where noted. (Test per ASTM D 1002-72.)

The separation rate of the testing jaws was 0.1in. per minute for metals, 2 in. per minute for plastics and 20 in. per minute for rubbers. The thickness of the substrates were: steel, 0.060 in.; other metals, 0.05-0.064 in.; rubber, 0.125 in.; plastics, 0.125 in.

Overlap Shear Strength (OLS) vs. Temperature

(Bonds cured 24 hours @ room temperature (RT) + 2 hours @ 160°F [71°C])

Bonds tested at:

-67°F(-55°C)

3000psi

70°F(21°C)

3500psi

120°F(49°C)

750psi

150°F(66°C)

400psi

180°F(82°C)

200psi

180° Peel Strength vs. Temperature

(Bonds cured 24 hours @ room temperature (RT) + 2 hours @ 160°F [71°C])

-67°F(-55°C)

2 piw

70°F(21°C)

13piw

120°F(49°C)

15piw

150°F(66°C)

2 piw

180°F(82°C)

1 piw

Solvent Resistance

OneHour/OneMonth

Acetone

A/A

IsopropylAlcohol

A/A

FreonTF

A/A

FreonTMC

A/A

1,1,1-Trichloroethane

A/A

RMAFlux

A/A

Key: A - Unaffected, B - Slight Attack, C - Moderate/Severe Attack

Exotherm

Max.Temp/TimetoReach

2 gram mass

128°F/6min.

20grammass

260°F/3min.

12 Overlap shear (OLS) strengths were measured on1 in. wide 1/2 in. overlap specimens. These bonds were made individually using 1 in. x 4 in. pieces of substrate. The thickness of the bond line was 0.005-0.008 in. All strengths were measured at 70°F (21°C) except where noted. (Test per ASTM D 1002-72.)

The separation rate of the testing jaws was 0.1in.per minute for metals,2 in. per minute for plastics and 20 in. per minute for rubbers. The thickness of the substrates were: steel, 0.060 in.; other metals, 0.05-0.064 in.; rubber, 0.125 in.; plastics, 0.125 in.

13 T-peel strengths were measured on1 in. wide bonds at 73°F (23°C). The testing jaw separation rate was 20 inches per minute.

The substrates were 0.020in.thick.(TestsperASTMD 1876-61T.)

14 Solvent resistance was determined using cured (24hrs. RT + 2 hrs. 160°F [71°C]) samples (1/2 in. x 4 in. x 1/8 in. thickness) immersed in the test solvent for 1 hour and 1 month. After the allotted period of time, the sample was removed and visually examined for surface attack as compared to the control.

Key: A - Unaffected - no change to color or surface texture.

B - Slight attack - noticeable swelling of surface.

C - Moderate/severe attack - extreme swelling of surface.