Permabond TA4605 is a two component, 1:1 toughened acrylic adhesive developed to bond low-surface energy plastics with no primer or surface treatment. It can also be used to bond a variety of other materials including composite or metal and is ideal for bonding dissimilar surfaces. 1:1 mix ratio by volume, Off-White, 50 mL Kit.

Great bonder for hard-to-bond surfaces like various rubbers, HDPE, UHMW, LDPE, LLDPE, polyolefins

Features and Benefits:

  • Adhesion to a wide variety of substrates
  • Thick Gel Formula, Thixotropic, Non-Sagging, Gap-Filling
  • Full cure at room temperature
  • Set time is 5-10 min
  • Bonds to polyolefins
  • No primer required
  • No need to flame-treat or plasma treat-surfaces before bonding
  • Excellent impact & sheer strength
  • Excellent chemical resistance

Ideal Surfaces / Works With:

  • Most Metals (Mild Steel, Stainless Steel, Aluminum, etc)
  • Most Plastics & In particular the hard-to-bond Low-Energy Plastics
  • Composites
  • Carbon Fiber
  • FRP (fiber reinforced plastics)
  • GRP (glass reinforced plastics)
  • ABS,
  • Polycarbonate
  • PVC
  • PA6
  • PET-G
  • PE-P
  • EPDM & Rubbers
  • E- Coatings
  • Polypropylenes (PPCO, PPHO, and related)
  • Polyethlyenes (LLDPE, LDPE, MDPE, HDPE, UHMW, etc)
  • PTFE / Nylon

Physical Properties of Uncured Adhesive

TA4605 A TA4605 B
Chemical Composition Methacrylate Methacrylate
Color Off-white Almost colorless
Mixed Color Off-white
Viscosity @ 25°C 150,000-400,000 mPa.s (cP) Thixo paste 20,000-30,000 mPa.s (cP)
Specific gravity 1.0 1.0

Typical Curing Properties

Ratio to Use 1:1
Maximum gap fill (NB: Contains microparticles to control gap) 1 mm (0.04 in)
Pot life (2g+2g) @23°C 2-4 minutes
Fixture time (0.1 N/mm² shear strength is achieved) @23°C 5-10 minutes
Handling time (0.3 N/mm ² shear strength is achieved) @23 °C 20-25 minutes
Working strength @23°C 2-4 hours
Full cure @23°C 24 hours

Comparable to 3M DP8005, DP 8010, and DP-8010