LORD 406/19 Fast Setting (4-6 Minute) Temperature Resistant, Non-Sag acrylic adhesives
In stock
Regular price
$ 26.99 USD
106 units available
Need Datasheets?
Click Here to visit our Datasheet Server (TDS, SDS, Fact Sheets, Selector Guides, etc)LORD 406/19 can be used to replace welding, brazing, riveting and other mechanical fastening methods. These adhesives perform particularly well in low-temperature environments and applications that are subject to high impact or high peel loads. LORD 403, 406 and 410 acrylic adhesives provide a range of working times to accommodate a wide variety of process requirements.
Fast Setting 6 to 10 minute set time (aka working life)
with a fast time to handling strength of 12 to 17 minutes
The 'GB' feature is code for Glass Microbead infused, which enables a controlled minimum bondline width.
Features and Benefits
- Versatile“ bonds a wide range of unprepared metals with minimal substrate preparation, as well as engineered thermoplastics including XENOY, polycarbonate, ABS and acrylics.
- Temperature Resistant performs at temperatures from -40 °F to +300° (-40°C to +149°C).
- Envirnomentally Resistant resists dilute acids, alkalis, solvents, greases, oils, moisture, salt spray and weathering; provides excellent resistance to indirect UV.
- Non-Sag remains in position when applied on vertical or overhead surfaces, allowing for greater process flexibility.
- UL Rated when mixed with LORD Accelerator 19, adhesive system is UL 746C certified.
Typical Properties
Appearance | Off-White to Tan Paste |
Viscosity, cP @ 77 °F (25 °C) | 100,000 – 300,000 |
Density, lb/gal (kg/m^3) | 9.1-9.7 (1090-1162) |
Flash Point, °F ( °C) | 59 (15) |
Typical Properties of Adhesive Mixed w/ Accelerator
Mix Ratio by Weight | 3.02:1 |
Mix Ratio by Volume | 4:1 |
Solids Content, % | 100 |
Working Time, min @ 75 °F (24 °C) | 6-10 |
Time to Handling Strength, min @ 75 °F (24 °C) | 12-17 |
Mixed Appearance | Tan Paste |
Cured Appearance | Tan to Green |
Typical Cured Properties
Tensile Strength at Break, psi (MPa) ASTM D638, modified |
4650 (32.1) |
Elongation, % ASTM D638, modified |
30 |
Young's Modulus, psi (MPa) ASTM D638, modified |
130,000 (896.3) |
Glass Transition Temperature, °F ( °C) ASTM E1640-99, by DMA |
162 (72) |
Visit our datasheet server to download a variety of documents for this formula, as well as for all other formulas and products that Perigee Direct carries.
And especially if you are considering or comparing a few different formulas. Our datasheet server can help you download the necessary data to help u decide and keep your project going.
Click Here to visit our Datasheet Server (TDS, SDS, Fact Sheets, Selector Guides, etc)