Permabond TA435 Acrylic Slow Set 30-60 min 130ml Kit & 300ml Cartridges
Need Datasheets? Need Accessories?
• Click Here to visit our Datasheet Server (TDS, SDS, Fact Sheets, Selector Guides, etc)• Check out Popular Accessories below by scrolling down just a bit on this page.
Regular price
$222.00 CAD
Call for ETA
PERMABOND TA435 is a structural acrylic adhesive designed primarily for bonding metals, ferrites, ceramics and some thermoplastics. This adhesive may be used in a variety of structural bonding applications, due to its versatile performance capabilities.
TA435 provides high strength while maintaining excellent flexibility, resulting in tough, durable bonds with outstanding impact and peel resistance. Handling strength is achieved in a few minutes at room temperature by using Permabond Initiator 41.
Features & Benefits
- Adhesion to a wide variety of substrates
- Fast cure at room temperature
- Set time is 30-60 min
- No mix application
- High shear and peel strength
- Good impact strength
- Good chemical resistance.
Table of Surface Activated Acrylic Adhesives, And the related Initiator Number that pairs with them
|
Grade |
TA430 and Initiator 41 or Initiator 41M |
TA435 and Initiator 41 or Initiator 41M |
TA436 and Initiator 43 |
TA437 and Initiator 41 or Initiator 41M |
TA439 and Initiator 41 or Initiator 41M* |
TA4590 and Initiator 44 |
TA4246 and Initiator 46 |
|
Color |
Amber |
Amber |
Amber |
Orange |
Amber |
Blue |
Amber |
|
Feature |
General Purpose |
High Peel Strength |
High Temp |
Anaerobic Cure |
Acid Free |
Acid Free |
MMA - very high strength |
|
Visc. cP 2.5 rpm |
50,000 |
70,000 |
60,000 |
130,000 |
- |
90,000 |
- |
|
Visc. cP 20 rpm |
20,000 |
30,000 |
25,000 |
40,000 |
1000 |
20,000 |
28,000 |
|
Specific Gravity |
1.1 |
1.0 |
1.1 |
1.1 |
1.0 |
1.1 |
1.0 |
|
Gap Fill inch (mm) |
0.02 (0.51) |
0.02 (0.51) |
0.02 (0.51) |
0.02 (0.51) |
0.006 (0.15) |
0.02 (0.51) |
0.02 (0.51) |
|
Handling Time |
3 - 5 min |
3 - 5 min |
1 - 3 min |
1 - 3 min 15 - 20 min** |
40 - 75 sec |
30 - 60 sec |
2 - 4 min |
|
Working Strength |
40 - 60 min |
30 - 60 min |
30 - 60 min |
30 - 60 min 60 - 120 min** |
3 - 5 min |
2 - 3 min |
15 - 30 min |
|
Full Cure |
24 hr |
24 hr |
24 hr |
24 hr |
24 hr |
24 hr |
24 hr |
|
Impact Strength |
10 - 15 kJ/m2 |
10 - 15 kJ/m2 |
10 - 15 kJ/m2 |
10 - 15 kJ/m2 |
10 - 20 kJ/m2 |
15 - 20 kJ/m2 |
50 - 60 kJ/m2 |
|
Shear Strength Steel |
2200-3600 psi 15 - 25 N/mm2 |
2200-3600 psi 15 - 25 N/mm2 |
2200-3600 psi 15 - 25 N/mm2 |
2000-3000 psi 14 - 20 N/mm2 |
2900-3600 psi 20 - 25 N/ mm2 |
2900-3600 psi 20 - 25 N/ mm2 |
4800-5100 psi 33 - 35 N/mm2 |
|
Peel Strength Aluminum |
10 - 14 PIW 45-65 N/25mm |
18 - 22 PIW 85-100 N/25mm |
10 - 14 PIW 45-65 N/25mm |
18 - 22 PIW 85-100 N/25mm |
18 - 22 PIW 85-100 N/25mm |
18 - 22 PIW 85-100 N/25mm |
33 - 40 PIW 150-180 N/25mm |
|
CTE |
80 x 10-6 1/K |
80 x 10-6 1/K |
80 x 10-6 1/K |
80 x 10-6 1/K |
80 x 10-6 1/K |
80 x 10-6 1/K |
80 x 10-6 1/K |
|
Thermal Conductivity |
0.1 W/(m.K) |
0.1 W/(m.K) |
0.1 W/(m.K) |
0.1 W/(m.K) |
0.1 W/(m.K) |
0.1 W/(m.K) |
0.1 W/(m.K) |
|
Dielectric Constant |
4.6 |
4.6 |
4.6 |
4.6 |
4.6 |
4.6 |
4.6 |
|
Dielectric Strength |
30 - 50 kVmm |
30 - 50 kVmm |
30 - 50 kVmm |
30 - 50 kVmm |
30 - 50 kVmm |
30 - 50 kVmm |
30 - 50 kVmm |
|
Volume Resistivity |
2 x 1013 Ohm.cm |
2 x 1013 Ohm.cm |
2 x 1013 Ohm.cm |
2 x 1013 Ohm.cm |
2 x 1013 Ohm.cm |
2 x 1013 Ohm.cm |
2 x 1013 Ohm.cm |
|
Temperature Range |
-65 to +250°F -55 to +120°C |
-65 to +250°F -55 to +120°C |
-65 to +300°F -55 to +150°C |
-65 to +390°F -55 to +200°C |
-65 to +330°F -55 to +165°C |
-65 to +330°F -55 to +165°C |
-40 to +250°F -40 to +120°C |