Product Name
Devcon 10760 Titanium Putty High-performance, Non-rusting Titanium-reinforced Epoxy
Brief Description
High-tech, titanium-reinforced epoxy putty engineered for making critical repairs to machinery and precision parts, designed to withstand heavy loads in hard chemical environments. It is non-rusting and can be precision machined after curing.
Popular Applications & Uses
- Restore bearing housings and scored shafts.- Rebuild wear rings, hydraulic rams, and valves.- Repair equipment and parts that require a machined finish.- Rebuilding pumps and other machinery.- Rebuild lost metal.- Protect new or repaired surfaces from cavitation, erosion, and corrosion.- Filling cracks and rebuilding damaged metal parts.
Industries that Commonly Use It
- Automotive Service/Repair- Chemical Industry- Energy- Engineering Services- Fabrication- General Manufacturing- Government & Military- Industrial Supply- Marine- Metal Fabrication- Petroleum Industry, Products or Services- Transportation/ Specialty Vehicle
Special and Unique Features
- Titanium-reinforced for high performance.- Non-rusting.- Can be precision machined after curing.- Withstands heavy loads in harsh chemical environments.- Qualifies under Mil Spec MIL-PRF-24176C, Type I.- Listed under NSN stock #8030-01-335-0562.- Formulated to be a dense mix for application to overhead and vertical surfaces without sagging.
Key Properties
- Color: Gray.- Excellent temperature resistance: up to 350°F (177°C) dry, 150°F (66°C) wet.- High compressive strength: 15,200 psi (105 MPa).- Resistance to chemicals and most acids, bases, solvents, and alkalis.- Hardness: 87 Shore D.- Working time (pot life): 21-24 minutes at 75°F (21-24°C).- Functional cure: 16 hours at 75°F (24°C).- Full cure: 7 days at 75°F.- Mix Ratio: 3.1:1 by volume; 4.3:1 by weight.- Shear Strength: 2,000 psi (13.8 MPa).- Specific Gravity: 2.36-2.5 g/cc.- Dielectric Strength: 56V/Mil (2205 volts/mm).
Surface Compatibility
- Metal (ferrous and non-ferrous).- Fiberglass.- Requires proper surface preparation: dry, clean, rough, degreased, free of paint, rust, grime.- Grit blasting or grinding to create a profile (75-125 micron desired).- Chemical cleaning after abrasive preparation.- Heating repair area in cold conditions is recommended for maximum adhesion.
Known backups / known substitutes
- Other metal-filled epoxies (e.g., stainless steel-filled, aluminum-filled).- Specific alternatives like SR-Titanium Steel Repair Putty (reinforced with titanium and stainless steel).- Gluespec provides resources for finding similar materials.
Comparison Note
Devcon 10760 Titanium Putty is distinguished by its titanium reinforcement, offering superior performance for critical repairs requiring precision machining, high compressive strength, and resistance to extreme temperatures and harsh chemicals, often exceeding the capabilities of general-purpose epoxies. Its qualification under military specifications highlights its robust and reliable nature for demanding applications.