Permabond TA4610 Polyolefin & Rubber Bonder Thick Gel 12-15 min Acrylic MMA Adhesive Off-White

In stock
SKU: PBND_TA4610_050ML
Cartridge or Starter Kit?
Regular price $64.00 AUD
5 units are available

Product details

  • Type Acrylic (MMA)
  • Vendor Permabond
  • SKU PBND_TA4610_050ML
  • Barcode TA04610K050C0101

Permabond TA4610 is a 2-part, 1:1 toughened acrylic adhesive. It has been developed to bond low surface energy plastics such as polypropylene and polyethylene - with no primer or expensive surface treatment required. It can also be used to bond a wide variety of other materials such as metals and composite materials and ideal for bonding dissimilar surfaces.

Features and Benefits:

  • Adhesion to a wide variety of substrates
  • Thick Gel Formula, Thixotropic, Non-Sagging, Gap-Filling
  • Full cure at room temperature
  • Set time is 12-15 min
  • Bonds to polyolefins
  • No primer required
  • No need to flame-treat or plasma treat-surfaces before bonding
  • Excellent impact & sheer strength
  • Excellent chemical resistance

Ideal Surfaces / Works With:

  • Most Metals (Mild Steel, Stainless Steel, Aluminum, etc)
  • Most Plastics & In particular the hard-to-bond Low-Energy Plastics
  • Composites
  • Carbon Fiber
  • FRP (fiber reinforced plastics)
  • GRP (glass reinforced plastics)
  • ABS,
  • Polycarbonate
  • PVC
  • PA6
  • PET-G
  • PE-P
  • EPDM & Rubbers
  • E- Coatings
  • Polypropylenes (PPCO, PPHO, and related)
  • Polyethlyenes (LLDPE, LDPE, MDPE, HDPE, UHMW, etc)
  • PTFE / Nylon

Physical Properties of Uncured Adhesive

TA4610 A TA4610 B
Chemical Composition Methacrylate Methacrylate
Color Off-white Almost colorless
Mixed Color Off-white
Viscosity @ 25°C 200,000-500,000 mPa.s (cP) Thixo paste 20,000-30,000 mPa.s (cP)
Specific gravity 1.0 1.0

Typical Curing Properties

Ratio to Use 1 : 1
Maximum gap fill (NB: Contains microparticles to control gap) 1 mm (0.04 in)
Pot life (2g+2g) @23°C 5-8 minutes
Fixture time (0.1 N/mm ² shear strength is achieved) @23°C 12-15 minutes
Handling time (0.3 N/mm ² shear strength is achieved) @23°C 40-50 minutes
Working strength @23°C 6-8 hours
Full cure @23°C 36-48 hours

Comparable to 3M DP8005, DP 8010, and DP-8010