LORD 406/19 Fast Setting (4-6 Minute) Temperature Resistant, Non-Sag acrylic adhesives

In stock
SKU: LORD_406/19_050ML_3021024
Size
Configuration
Regular price $42.00 AUD
32 units available
32 units are available

LORD 406/19 can be used to replace welding, brazing, riveting and other mechanical fastening methods. These adhesives perform particularly well in low-temperature environments and applications that are subject to high impact or high peel loads. LORD 403, 406 and 410 acrylic adhesives provide a range of working times to accommodate a wide variety of process requirements.

Fast Setting 6 to 10 minute set time (aka working life)

with a fast time to handling strength of 12 to 17 minutes

The 'GB' feature is code for Glass Microbead infused, which enables a controlled minimum bondline width.

Features and Benefits

  • Versatile“ bonds a wide range of unprepared metals with minimal substrate preparation, as well as engineered thermoplastics including XENOY, polycarbonate, ABS and acrylics.
  • Temperature Resistant performs at temperatures from -40 °F to +300° (-40°C to +149°C).
  • Envirnomentally Resistant resists dilute acids, alkalis, solvents, greases, oils, moisture, salt spray and weathering; provides excellent resistance to indirect UV.
  • Non-Sag remains in position when applied on vertical or overhead surfaces, allowing for greater process flexibility.
  • UL Rated when mixed with LORD Accelerator 19, adhesive system is UL 746C certified.

Typical Properties

Appearance Off-White to Tan Paste
Viscosity, cP @ 77 °F (25 °C) 100,000 – 300,000
Density, lb/gal (kg/m^3) 9.1-9.7 (1090-1162)
Flash Point, °F ( °C) 59 (15)

 

Typical Properties of Adhesive Mixed w/ Accelerator

Mix Ratio by Weight 3.02:1
Mix Ratio by Volume 4:1
Solids Content, % 100
Working Time, min @ 75 °F (24 °C) 6-10
Time to Handling Strength, min @ 75 °F (24 °C) 12-17
Mixed Appearance Tan Paste
Cured Appearance Tan to Green

 

Typical Cured Properties

Tensile Strength at Break, psi (MPa)
ASTM D638, modified
4650 (32.1)
Elongation, %
ASTM D638, modified
30
Young's Modulus, psi (MPa)
ASTM D638, modified
130,000 (896.3)
Glass Transition Temperature, °F ( °C)
ASTM E1640-99, by DMA
162 (72)