CS-NRI EPN-101 two-part epoxy paste filler (aka EPN-101-1PT or EPN-101-13OZ)

In stock
SKU: CSNRI_EPN-101-1PT
Size
Regular price $566.00 AUD
Currently Out of Stock Call for ETA
Currently Out of Stock Place Order and Call for ETA

The CS-NRI EPN-101 is a solvent free, chemically resistant, two-part bulk epoxy paste filler used to fill and transition surface irregularities including pits, voids, corrosion defects, dents, leak repair “stopgaps”, etc. Its high-build capability allows technicians to transition aggressive changes in geometry without multiple lifts. Once cured, EPN-101 is machinable.

Benefits

  • High-build capability without slumping or sagging
  • Can be over-coated as soon as it is dry to the touch
  • Resistant to a wide variety of inorganic acids, alkalis, salts and organic media
  • Machinable once cured

Applications

  • Any metal surface defect containing pits, voids, corrosion, etc.
  • Used in conjunction with patches, plugs and other leak repair techniques
  • Used to transition aggressive changes in geometry or large defects prior to installing ECR Systems

Storage
Store indoors in cool, dry, ventilated storage at temperatures below 35°C (95°F ) in original, unopened containers. Minimum storage temperature 15.5°C (60°F)

Limitations

  • Epoxy application temperature: minimum of 5°C (40°F) or less than 3°C (37°F) above dew point
  • Base component should be warmed to 15.5°C to 25°C (60 to 77°F) before mixing
  • Over-coating time should not exceed 3 hours
  • Suitable for long-term immersion at temperatures up to 70°C (158°F) and intermittent contactwith pressurized steam up to 120°C (248°F)
  • Resistant to dry heat in excess of 200°C (392°F) dependent on load

Material Properties

TEST RESULT

Hardness, Rockwell R 100

Hardness, Shore D 90

Compressive Strength @ 75°F (24°C) 19,400 psi (133.8 MPa)

Compression Modulus @ 75°F (24°C) 511 ksi (3,524 MPa)

Tensile Shear Adhesion 2,630 psi (18.2 MPa)

Flexural Strength 10,000 psi (68.9 MPa)

Corrosion Resistance 5,000 hours

Glass Transition Temperature (Tg) 240°F (116°C) With 248°F (160°C) Cure

Heat Distortion Temperature 136°F (58°C) With 68°F (20°C) Cure

Heat Distortion Temperature 208°F (98°C) With 212°F (100°C) Cure